JINING XUNDA PIPE COATING MATERIALS CO.,LTD

Products > Pipe Coating System > > XUNDA en 12068 C 50 coating system
Product name : XUNDA en 12068 C 50 coating system
Film : polyethylene
Adhesive : butyl rubber
Release paper : 
Standard : EN 12068
Storage life : 24 months
 Enlarge Image                   Back
←[Previous Product]              [Next Product]→


Details:

EN 12068 C 50 coating system

XUNDA EN12068 C50 Coating system consists of Primer +3ply inner tape + 2 ply outer tape . The primer is 27% solid content,
 the 3 ply inner tape thickness is 30 mils, the 2 ply outer tape thickness is 20 mils. Totally 50 mils

 

The primer is called liquid adhesive,anti corrosion paint,primer coat,anti-corrosive glue.

It consisting of butyl based elastomers blended polymeric resins dissolved in an organic solvent. The XUNDA primer suitable for 
hand brush application to rough,reconditioned or grit-blasted pipe surface. It Similar to  American Polyken,DENSO product. 
The usage is to provide a bonding medium between the primed pipe surface and the inner tape

 

 

Properties

Unit

P27

 Test Method

Solid content 

%

27

ISO 3251

Density

Kg/liter

0.87

ISO 2811-1

Viscosity+23℃

(out flow time,4mm nozzle)

sec

40±5

ASTM D 1200

Flash point

12

ISO 1523

Drying time 

min

5-10

--

Color 

 

Black

Visual

Application temperature

-10 -  80

Package

3.8/10/18/20 Liter per drum

 

 

 

3 Ply inner tape. It also be called double sided tape, double coated tape,three ply inner wrapping

System description:

 

The XUNDA-T400 series is Cold applied tape coating system for corrosion protection of Oil, Gas, Petrochemical, and Waste Water 
underground or overhead pipelines

It is a three-ply cold applied tape with stabilised polyethylene bcking and butyl rubber adhesive layers on both sides.It is also used as
 inner-layer tape. It 
shall be applied by hand or with a wrapping machine

 

The 3 Ply tape shall be applied after the Liquid adhesive and before the outer-layer tape by hand or with a wrapping machine

 

Structure

The specification of the tape consists of four layers,

Internal Adhesive layer:Butyl rubber 

External Adhesive layer: Butyl rubber

Film backing:Special blend of stabilized polyolefines

Interleaf:Antiadhesive Film Treated with Silicone

 

Features:

Excellent bonding between adhesive and carrier film via co-extruded intermediate layer. 

Mechanically highly resistant tape system.

Practically impermeable to water vapour and oxygen. 

Resistant to soil bacterial and soil electrolyte. 

Compatible with coating from PE,PP,FBE,PU,CTE and Bitumen and ext… . 

A Total Coating System with:

High adhesion and shear resistance

Resistance to corrosion disbondment

High electrical resistance

High dielectric strength

High corrosion protection for steel substrates

 

 Physical Properties

 

XUNDA-T 480

 

Physical Properties

 

Test Method

Typical Value

English

Metric

Color film backing
Adhesive inner layer
Adhesive outer layer

--

black(grey/green)
black 
black

Thickness Carrie film
Internal Adhesive
External Ahesive

 

 

ASTM D 1000

12.0 mil

13.6 mil

6.4 mil

0.30mm

0.34 mm

0.16 mm

Total thickness

32.0 mil

0.80 mm

Tensile strength

ASTMD1000

70 lbs/in

120 N/cm

Elongation at break

ASTMD1000

650%

Peel strength to primed steel at 23 

at 50℃

EN 12068

Annex C

274.5 oz/in

137.1 oz/in

30 N/cm

15 N/cm

Peel strength tape to tape at  23 ℃                         at 50℃

EN 12068

Annex B

228 oz/in

32 oz/in

25 N/cm

3.5 N/cm

Dielectric strength

ASTMD149

35 Kv

Insulation    Resistance

EN 12068

108 ohm·

Water Vapor Transmission Rate 24h

ASTM E 96

0.01g/100sq in/24h

0.1g/100sq mm/24h

Brittleness temperature

DIN53372

-51±39

-46±4 ℃

Water Absorption

ASTM D 570

0.08 %

Impact resistance at 23°

EN 12068

15 J

Cathodic disbandment at 23°c

at 50°c

 

EN 12068

15 mm

30 mm

Lap shear strength   at 50

EN 12068

0.05 N/mm2

 

 

2 ply outer tape, it is also be called outer wrapping tape, outer wrap, mechanical protection tape

System description:

The XUNDA-T200 series is Cold applied tape coating system for corrosion protection of Oil, Gas, Petrochemical, and Waste Water 
underground or overhead pipelines. The outer tape backing shall be compounded so that it will be resistance to outdoor weathering.

 

The outer tape shall be applied after the inner tape by hand or with a wrapping machine

 

Structure:

 

The specification of the tape consists of two layers, adhesive layer and film backing

Adhesive: butyl rubber 

Film backingr: Special blend of stabilized polyethylene

 Features:

 

Excellent adhesion to inner tape and self

Resistant to UV

Can be applied over a wide temperature range 

Good conformability and consistent uniform thickness

Easily applied with no special equipment

Compatible with common pipe coatings

Excellent resistance to cathodic disbonding

Meets ASTM D 1000 Standard

Cold applied

Physical Properties:

 

XUNDA-T 250 =Polyken 955-20 

 

Physical Properties

 

Test Method

Typical Value

English

Metric

Total thickness

ASTM D 1000

20.0 mil

0.50mm

Backing thickness 

ASTM D 1000

13.0 mil

0.32 mm

Adhesive thickness 

ASTM D 1000

7.0 mil

0.18 mm

Width 

-

2’’- 32 ‘’

50 -800 mm

Length 

-

100 -800 

30 -240 m

Backing colour

-

White

Tensile strength 

ASTM D 1000

70 N/ cm

Elongation

ASTM D 1000

400 %

Peel Adhesion to inner tape

ASTM D 1000

5 N/cm

Cathodic Disbandment

ASTM G8

0.25 in radius 6.4 mm

Dielectric Strength 

ASTM D 149

40 Kv

Volume Resistivity 

ASTM D 257

2.0x1012 ohm.cm

Water Absorptivity

ASTM D 570

0.1 %

Water Vapor Transmission Rate 24h

ASTM F1249

0.1g/100sq mm/24h

UV resistance

-

Excellent

Application Temperature                                                                        

-

-10 ℃ - 60 ℃

Max Service Temperature

-

- 40  - 80

 

How to install it ?

Metal Surface Condition:

 

Bare pipe shall be free from mud, mill scale, mill lacquer, wax, coal tar, asphalt, oil, grease, or any other foreign material. Before blast 
cleaning, surfaces shall be inspected and pre-cleaned according to SSPC-SP 1 to remove oil, grease, and loosely adhering deposits.
 Visible oil and grease spots shall be removed using a solvent. Only solvents that do not leave a residue shall be used. Preheating to 
remove oil, grease, and mill scale may be used provided that all pipe is preheated in a uniform manner to avoid distortion.

Liquid Adhesive Application

 

The liquid adhesive shall be applied in a uniform thin at the coverage rate recommended by the manufacture. The liquid adhesive shall
 be thoroughly and continuously mixed and agitated during application to prevent settling. The liquid adhesive may be applied  to the 
entire exterior surface of the pipe by spray-type or rug-type methods or other suitable means to cover the entire exterior surface of the 
pipe. The liquid adhesive coat shall be uniform and free from floods, runs, sags, drips, or bare spots. The liquid adhesive coated pipe 
surface shall be free of any foreign substances, such as sand, grease, oil, grit, rust particles, or dirt. Before applying the inner-layer-tape, the liquid adhesive layer shall be allowed  to dry in accordance with the manufacturer's recommendation.

 

Application of Inner-layer-tape

 

The inner-layer tape shall be applied directly onto the prepared pipe surface using mechanical constant tension coating equipment. 
The inner layer tape shall be spirally applied with overlap width and application tension as recommended by manufacture. 
When applied to spirally welded pipe , the direction of the tape spiral shall be generally parallel to the weld spiral. The minimum 
overlap shall not be less than 25 mm. When a new row of tape is started, the ends shall be overlapped at least 150 mm measured 
circumferentially.

 

 

Application of Outer-layer-tape

 

The Outer-layer tape shall be applied over the inner -layer tape using the same type of mechanical equipment used to apply the 
inner-layer tape. The overlap of the outer-layer tape shall not coincide with the overlap of the inner-layer tape. The minimum overlap 
of the applied tape and minimum end lap of two rolls shall be the same as that of inner-layer tape. The outer-layer tape shall be applied 
at minimum roll temperature of 21 
. The tape manufacture shall be consulted for recommended temperature of roll above 21  to
 enhance conformability of the outer-wrap to the pipe surface.

 

 

Company information:

Industries that We Serve 

Oil, Gas and Water Transmission pipeline market

Oil and Gas distribution and utility markets

New pipeline construction markets

Rehabilitation and Reconditioning market

Offshore Industry

Refinery and Petrochemical Plant Industry

Manufacture of Polyethylene coatings utilizing Butyl based elastomeric adhesives, Polyethylene films and liquid adhesives for 
corrosion protection of steel pipe.

Provides corrosion protection with the inherent chemistry of Polyethylene and Butyl Adhesive for resistance to water and oxygen 
penetration. Oxygen and Water are prevented from reaching the metal substrate, which are necessary and sufficient conditions for 
corrosion.

Manufacture of conventional and specialty Polyethylene, Polypropylene and Polymeric Alloys and coating systems for pipe corrosion
 protection.

Manufactures PE coatings systems for applications for New Pipe Construction and Rehabilitation and Reconditioning

Approved to ISO 9001 and to other good manufacturing and technical standards and norms governed within the energy and pipeline
 industry.

Coating systems that have a broad range of temperature and shear resistance properties to meet the requirements of the pipeline and
 end-user.

 


Related Products :
Black & white Pipe Wrapping tape for natural gas pipe

Black & white Pipe Wrapping tape for natural gas pipe
CHINA pipe Anti corrosion tape similar with Berry plastic 980-20
T 150
CHINA pipe Anti corrosion tape similar with Berry plastic 980-20
anti-corrosion protective coating system

anti-corrosion protective coating system
PE Wrap Tape

PE Wrap Tape
Viscoelastic body Anti corrosion adhesive tape

Viscoelastic body Anti corrosion adhesive tape
XUNDA multilayer coating system

XUNDA multilayer coating system
AWWA C 214 pipe coating system

AWWA C 214 pipe coating system
Water Pipe Wrapping adhesive tape

Water Pipe Wrapping adhesive tape