POLYTHYLENE COATING &WRAPPING OF UNDERGROUND PIPING

A) Laminated polyethylene (low-density), backed self-adhesive, rubberized, bitumastic compound tape. 

1) Polyethylene inner wrap: 

Thickness should be minimum 0.305 mm (0.012"), with self-adhesive compound thickness 0.203 mm (0.008") minimum. Interleaf in rolls supplied shall be double sided release coated paper or polymer preferably with extra width for roll protection. Final thickness should be defined as Characteristics of tape: 

- Elongation : 250% 

- Tensile strength : 7 N/mm2 

- Tear resistance : 8 kg/cm 

- Dielectric strength : 40 Kvolt/mm 

- Insulation strength : 1 x 106 Ohm/mm 

- Impact resistance : 3.2 Joules 

- Adhesion to steel (With primer) : 2.6 N/mm 

- Adhesion to self : 0.5 N/mm 

- Temperature range : -5C to 90

2) Polyethylene outer wrap : 

Thickness should be minimum 0.229 mm (0.009") with 0.102 mm (0.004") self-adhesive 

compound. Polyethylene to be White or Silver-Grey light reflecting. Final thickness should 

be defined as per vendor data. 

Characteristics of tape: 

- Elongation : Min 200% 

- Dielectric strength : Min. 10 KVolt 

- Insulation resistance : 1x1012Ohm/in 

b) Bitumen solution type primer, fast drying (3 to 10 minutes). 

c) Molding Putty 

A compatible molding putty to the supplied tape shall be provided for applying around fittings and flanges, etc., supplied in drums.

 

Roll widths of wrapping tapes to be used shall be conform to the table below: 

 

TAPE WIDTH (MM) 

PIPES 

BENDS 

TEES 

FLANGES 

150 

Up to 3" 

Up to 8" 

Up to 12" 

All 

100 

4" to 8" 

10" to 24" 

14" and above 

150 

10" to 16" 

28" and above 

225 

18" and above